Fabrication and laser oscillation of Yb:Sc2O3 transparent ceramics from co-precipitated nano-powders

Anno: 2018

Autori: Dai ZF., Liu Q., Toci G., Vannini M., Pirri A., Babin V., Nikl M., Wang W., Chen HH., Li J.

Affiliazione autori: Key Laboratory of Transparent and Opto-functional Inorganic Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China; School of Material Science and Engineering, Jiangsu University, Zhenjiang 212013, China; C.N.R – National Research Council, Istituto Nazionale di Ottica, Via Madonna del Piano 10, (FI), I-50019 Sesto Fiorentino, Italy; C.N.R – National Research Council, Istituto di Fisica Applicata Nello Carrara Via Madonna del Piano 10, (FI), I-50019 Sesto Fiorentino, Italy; Institute of Physics Academy of Sciences of the Czech Republic, Cukrovarnicka 10, Prague 162 53, Czech Republic

Abstract: Ytterbium doped scandium oxide (Yb:Sc2O3) transparent ceramics were fabricated by a co-precipitation and vacuum sintering method. The characteristics of the precursor and the calcined powders were investigated by BET, XRD, and SEM. Ultra-fine and low agglomerated 5at%Yb:Sc2O3 powders with the average particle size about 65.4 nm were obtained after calcined at 1100 degrees C for 5 h. Using the synthesized powders as starting materials, 5at%Yb:Sc2O3 transparent ceramics with the in-line transmittance of 71.1% at 1100 nm and average grain size of 145 pm were fabricated by vacuum sintering at 1825 degrees C for 10 h. Quasi-CW laser oscillation of Yb:Sc2O3 ceramics was obtained at 1040.6 nm. A maximum output power as high as 2.44 W with a corresponding slope of 35% was achieved. Finally, the tunability of the ceramic was explored measuring a tuning range up to 55 nm.

Giornale/Rivista: JOURNAL OF THE EUROPEAN CERAMIC SOCIETY

Volume: 38 (4)      Da Pagina: 1632  A: 1638

Maggiori informazioni: This work was supported by the National Natural Science Foundation of China (Grant No. 61575212 ), the Key research project of the frontier science of the Chinese Academy of Sciences (No. QYZDB-SSW-JSC022 ), the National key R&D Program of China ( 2017YFB0310502 ), and the Short Term Mobility Program 2016 of the National Research Council of Italy .
Parole chiavi: Co-precipitated nano-powders; Fabrication; Laser performance; Transparent ceramics; Yb:Sc2O3; Calcination; Ceramic materials; Continuous wave lasers; Particle size; Powders; Sintering; Vacuum applications; Ytterbium, Average grain size; Average particle size; Laser oscillations; Laser performance; Maximum output power; Nano powders; Synthesized powder
DOI: 10.1016/j.jeurceramsoc.2017.10.027

Citazioni: 19
dati da “WEB OF SCIENCE” (of Thomson Reuters) aggiornati al: 2024-04-14
Riferimenti tratti da Isi Web of Knowledge: (solo abbonati)
Link per visualizzare la scheda su IsiWeb: Clicca qui
Link per visualizzare la citazioni su IsiWeb: Clicca qui