High surface area carbonous components from emulsion derived SiOC and their gas sensing behavior
Autori: Vakifahmetoglu C., Buldu M., Karakuscu A., Ponzoni A., Assefa D., Soraru G. D.
Affiliazione autori: – Department of Mechanical Engineering, Istanbul Kemerburgaz University, 34217 Istanbul, Turkey
– SENSOR Lab, CNR-INO and Department of Information Engineering, University of Brescia, Brescia, Italy
– Dipartimento di Ingegneria Industriale, Università di Trento, Via Sommarive 9 38123 Trento, Italy
Abstract: A commercially available liquid polysiloxane polymer was emulsified via stirring in the presence of water and surfactant. After curing, porous microbead/capsule thermosets were obtained. The samples kept their shape upon pyrolysis and resulted in SiOC ceramics which were etched by hydrofluoric acid at room temperature. The specific surface area of the components increased considerably reaching to 310 m(2)/g when etching process was conducted. It was shown that the samples had hierarchical porosity including micro-meso and macro porosity (5-10 micron range). The etching process affected the conductivity and the room temperature NO2 sensing capability of the SiOC samples. It is shown that porous SiOC and carboneous materials produced via hydrofluoric acid etching, can be used to detect NO2 (5 ppm) at room temperature (for the etched sample) with an easy-to-read conductance (mS range) as well as fast response kinetics (few minutes) and a complete signal recovery. (C) 2015 Elsevier Ltd. All rights reserved.
Giornale/Rivista: JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
Volume: 35 (16) Da Pagina: 4447 A: 4452
Maggiori informazioni: C.V. and M.B. gratefully acknowledge the support of TUBITAK (The Scientific and Technological Research Council of Turkey) under the project Grant No: CAYDAG-113Y533.Parole chiavi: Preceramic polymers; Porous ceramic beads; High surface area; Gas sensing; DOI: 10.1016/j.jeurceramsoc.2015.08.030Citazioni: 36dati da “WEB OF SCIENCE” (of Thomson Reuters) aggiornati al: 2023-03-19Riferimenti tratti da Isi Web of Knowledge: (solo abbonati) Link per visualizzare la scheda su IsiWeb: Clicca quiLink per visualizzare la citazioni su IsiWeb: Clicca qui