Fabrication, microstructure, and optical properties of Yb:Y3ScAl4O12 transparent ceramics with different doping levels

Anno: 2020

Autori: Feng YG., Toci G., Pirri A., Patrizi B., Hu ZW., Wei JB., Pan HM., Zhang X., Li XY., Su S., Vannini M., Li J.

Affiliazione autori: Chinese Acad Sci, Shanghai Inst Ceram, Key Lab Transparent Optofunct Inorgan Mat, Shanghai 201899, Peoples R China; Univ Chinese Acad Sci, Ctr Mat Sci & Optoelect Engn, Beijing, Peoples R China; CNR, INO, Sesto Fiorentino, FI, Italy; IFAC, CNR, Sesto Fiorentino, FI, Italy; CNR, INO, Pisa, Italy; Jiangsu Univ, Sch Mat Sci & Engn, Zhenjiang, Jiangsu, Peoples R China

Abstract: Transparent Yb:Y3ScAl4O12 (Yb:YSAG) ceramics with different ytterbium doping concentrations such as 5, 10, 15, 20 at.% have been successfully fabricated by solid-state reactive sintering. All the obtained ceramics are in dense and homogeneous structure after sintering at 1820 degrees C for 30 hours and with a posttreatment by hot isostatic pressing at 1750 degrees C for 3 hours with 200 MPa pressure. We systematically analyzed the influence of Yb3+ doping concentration on the microstructure and optical properties of the ceramics. The 10 at.% Yb:Y3ScAl4O12 ceramics with a thickness of 3.2 mm show the best transparency as high as 80.9% at 1100 nm. The laser emission of the 10 at.% Yb:YSAG ceramics was tested, resulting in a maximum slope efficiency of 67.6% and a maximum output power of 11.3 W under quasi-continuous wave pump conditions. The tuning range spanned from 990 to 1071 nm.


Volume: 103 (1)      Da Pagina: 224  A: 234

Parole chiavi: optical properties; transparent ceramics; Yb; Y3ScAl4O12 (Yb; YSAG); ytterbium concentration
DOI: 10.1111/jace.16691

Citazioni: 10
dati da “WEB OF SCIENCE” (of Thomson Reuters) aggiornati al: 2022-01-23
Riferimenti tratti da Isi Web of Knowledge: (solo abbonati)
Link per visualizzare la scheda su IsiWeb: Clicca qui
Link per visualizzare la citazioni su IsiWeb: Clicca qui

This site uses cookies. If you decide to continue browsing we consider that you accept their use. For more information about cookies and how to delete them please read our Info Policy on cookies use.
Read more